Cross-linking of dermal sheep collagen using a water-soluble carbodiimide

Share/Save/Bookmark

Olde Damink, L.H.H. and Dijkstra, P.J. and Luyn van, M.J.A. and Wachem van, P.B. and Nieuwenhuis, P. and Feijen, J. (1996) Cross-linking of dermal sheep collagen using a water-soluble carbodiimide. Biomaterials, 17 (8). pp. 765-773. ISSN 0142-9612

[img]
Preview
PDF
1101Kb
Abstract:A cross-linking method for collagen-based biomaterials was developed using the water-soluble carbodiimide 1-ethyl-3-(3-dimethyl aminopropyl)carbodiimide hydrochloride (EDC). Cross-linking using EDC involves the activation of carboxylic acid groups to give O-acylisourea groups, which form cross-links after reaction with free amine groups. Treatment of dermal sheep collagen (DSC) with EDC (E-DSC) resulted in materials with an increased shrinkage temperature (Ts) and a decreased free amine group content, showing that cross-linking occurred. Addition of N-hydroxysuccinimide to the EDC-containing cross-linking solution (E/N-DSC) increased the rate of cross-linking. Cross-linking increased the Ts of non-cross-linked DSC samples from 56 to 73 °C for E-DSC and to 86 °C for E/N-DSC samples, respectively. For both cross-linking methods a linear relation between the decrease in free amine group content and the increase in Ts was observed. The tensile strength and the high strain modulus of E/N-DSC samples decreased upon cross-linking from 18 to 15MPa and from 26 to 16MPa, respectively. The elongation at break of E/N-DSC increased upon cross-linking from 142 to 180%.
Item Type:Article
Copyright:© 1996 Elsevier Science
Faculty:
Science and Technology (TNW)
Research Group:
Link to this item:http://purl.utwente.nl/publications/9854
Official URL:http://dx.doi.org/10.1016/0142-9612(96)81413-X
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 105371