Alternating polyesteramides based on 1,4-butylene terephthalamide: 3. Alternating polyesteramides based on mixtures of linear diols (4NTm,p)

Share/Save/Bookmark

Serrano, P.J.M. and Werff, B.A. van der and Gaymans, R.J. (1998) Alternating polyesteramides based on 1,4-butylene terephthalamide: 3. Alternating polyesteramides based on mixtures of linear diols (4NTm,p). Polymer, 39 (16-18). pp. 83-92. ISSN 0032-3861

[img] PDF
Restricted to UT campus only
: Request a copy
934kB
Abstract:Strictly alternating polyesteramides consisting of 1,4-butylene terephthalamide diester and mixtures of aliphatic diols have been synthesised in the melt in the presence of a titanium catalyst. To increase the molecular weight a solid state post condensation was applied. The composition was determined with 1H NMR. The thermal properties were analysed with differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis (DMTA). With the mixture of diols the structural regularity of the diester part in polymers was disturbed. Although this disturbance caused the polymers to be fast crystallising (ΔT < 32°), highly crystalline polymers. It was found that the melting temperature decreased linearly with increasing length of the diols in the mixture. The melting temperatures with the mixtures of diols were lower than with a single diol. The reason for this is probably thinner lamella. Mechanical tests on the melt processed polyesteramides showed high glass transition temperatures and a high modulus above the glass transition temperature. These polyesteramides have a Tg/Tm ratio of 0.70–0.72. This high ratio is probably due to the relatively low melting temperatures. The water absorption, is close to the values for polyesters (1.3–1.7 wt%). Disturbing the alternating structure of the polyesteramide by esteramide interchange reactions resulted in a loss of the thermal and mechanical properties.
Item Type:Article
Copyright:© 1998 Elsevier
Research Group:
Link to this item:http://purl.utwente.nl/publications/73825
Official URL:http://dx.doi.org/10.1016/S0032-3861(97)00232-2
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 105667