Superplastic deep drawing of tetragonal zirconia ceramics at 1160°C

Share/Save/Bookmark

Winnubst, A.J.A. and Boutz, M.M.R. (1998) Superplastic deep drawing of tetragonal zirconia ceramics at 1160°C. Journal of the European Ceramic Society, 18 (14). pp. 2101-2106. ISSN 0955-2219

[img] PDF
Restricted to UT campus only
: Request a copy
574kB
Abstract:Superplastic forming under biaxial tension of tetragonal zirconia (Y-TZP) is investigated by pushing a hemispherical punch (radius 6 mm) on Y-TZP which was placed on a ring with an inner diameter of 16·7 mm. Dense Y-TZP samples with a grain diameter of 125 nm could be elongated to a dome height of at least 8 mm at a temperature as low as 1160°C. Such elongations could not be achieved at this very low temperature when the ceramic had a grain diameter of 250 nm. At a grain size of 250 nm differences in deformation behaviour were observed for different types of Y-TZP powders. This is explained by the fact that at higher cavity concentration in the sintered compact the sample deforms at lower forces but fractures at lower elongations.
Item Type:Article
Faculty:
Science and Technology (TNW)
Research Group:
Link to this item:http://purl.utwente.nl/publications/72308
Official URL:http://dx.doi.org/10.1016/S0955-2219(98)00144-7
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 106516