Romanyuk, Y.E. and Ehrentraut, D. and Aznar, A. and Sole, R. and Aguilo, M. and Gerner, P. and Güdel, H.U. and Pollnau, M. (2003) Liquid phase epitaxy and optical investigation of KYb(WO4)2 thin layers. In: 4th International Spring Workshop on Spectroscopy, Structure & Synthesis of Rare Earth Systems, 21-26 June 2003, Ladek Zdroj, Poland (pp. O22).
|Abstract:||In recent years, Yb3+ has attracted much attention as an activating ion because of its small quantum defect for laser emission from 2F5/2 to 2F7/2 at ~1.03 µm , which provides high efficiency and reduced heat generation. Of high practical interest is the thin-disk laser concept , which possesses a tremendous advantage over rod lasers because of its axial-cooling approach and consequent weak thermal lensing and good beam quality.
A promising material for Yb3+ thin-disk lasers is KYb(WO4)2 (KYbW) . It can be grown from high-temperature solutions . Nevertheless, the growth of high-quality, single-crystalline layers with thickness in the range of the absorption length of ~13 µm at 981 nm has as yet not been reported. A suitable substrate material is KY(WO4)2 (KYW), but the relatively large differences in the thermal expansion coefficients between KYW and KYbW along the , , and especially  directions  favor low temperatures for the hetero-epitaxial growth.
For the first time, we demonstrate liquid phase epitaxy (LPE) of KYbW layers. The layers were grown at start temperatures as low as 520°C, which is favorable in order to decrease the thermal stresses due to the differences in the thermal expansion coefficients of substrate and layer. Moreover, the choice of -oriented substrates bypasses the large difference in the thermal expansion coefficient along the  direction. KY1-xYbx(WO4)2 layers with varying x = 0.03-1.00 were grown by LPE. The chloride solvent consisted of the eutectic composition  24.4 mol.% KCl, 30.4 mol.% NaCl, and 42.2 mol.% CsCl. The growth temperature spanned the range from 580 to 500°C and the cooling rate was 0.67-1.00 Kh-1. Crack-free, transparent KYbW layers were grown on (010) substrates.
Spectroscopic investigations have shown that the lifetime of ~250 µs measured in our LPE-grown KYbW layers is dominated by radiative decay and is very similar to that measured in top-seeded-solution-grown bulk samples . Fast energy migration among the Yb3+ ions and energy transfer to small amounts of Tm3+ and Er3+ ions present in the YbCl3 reagent lead to visible upconversion luminescence in the layers under 981-nm excitation.
 T.Y. Fan, IEEE J. Quantum Electron. 29, 1457 (1993).
 A. Giesen, H. Hügel, A. Voss, K. Wittig, U. Brauch, H. Opower, Appl. Phys. B 58, 365 (1994).
 P. Klopp, U. Griebner, V. Petrov, X. Mateos, M.A. Bursukova, M.C. Pujol, R. Solé, J. Gavaldà, M. Aguiló, F. Güell, J. Massons, T. Kirilov, F. Díaz, Appl. Phys. B 74, 185 (2002).
 M.C. Pujol, M.A. Bursukova, F. Güell, X. Mateos, R. Solé, J. Gavaldà, M. Aguiló, J. Massons, F. Díaz, P. Klopp, U. Griebner, V. Petrov, Phys. Rev. B 65, 165121 (2002).
 M.C. Pujol, X. Mateos, R. Solé, J. Massons, J. Gavaldà, F. Díaz, M. Aguiló, Mater. Sci. Forum 378-381, 710 (2001).
 D. Ehrentraut, M. Pollnau, S. Kück, Appl. Phys. B 75, 59 (2002).
|Item Type:||Conference or Workshop Item|
|Link to this item:||http://purl.utwente.nl/publications/72144|
|Export this item as:||BibTeX|
Daily downloads in the past month
Monthly downloads in the past 12 months
Repository Staff Only: item control page