Morphology and melt rheology of nylon 11/clay nanocomposites


He, Xiaofeng and Yang, Jun and Zhu, Lianchao and Wang, Biao and Sun, Guangping and Lv, Pengfei and Phang, In Yee and Liu, Tianxi (2006) Morphology and melt rheology of nylon 11/clay nanocomposites. Journal of Applied Polymer Science, 102 (1). pp. 542-549. ISSN 0021-8995

open access
[img] PDF
Abstract:Nylon 11 (PA11)/clay nanocomposites have been prepared by melt-blending, followed by melt-extrusion through a capillary. Transmission electron microscopy shows that the exfoliated clay morphology is dominant for low nanofiller content, while the intercalated one is prevailing for high filler loading. Melt rheological properties of PA11 nanocomposites have been studied in both linear and nonlinear viscoelastic response regions. In the linear regime, the nanocomposites exhibit much higher storage modulus (G') and loss modulus (G'') values than neat PA11. The values of G' and G'' increase steadily with clay loading at low concentrations, while the G' and G'' for the sample with 5 wt % clay show an inverse dependence and lie between the modulus values of the samples with 1 and 2 wt % of clay. This is attributed to the alignment/orientation of nanoclay platelets in the intercalated nanocomposite induced by capillary extrusion. In the nonlinear regime, the nanocomposites show increased shear viscosities when compared with the neat resin. The dependence of the shear viscosity on clay loading has analogous trend to that of G' and G''. Finally, a comparison has been made between the complex and steady viscosities to verify the applicability of the empirical Cox-Merz rule.
Item Type:Article
Copyright:© 2006 Wiley InterScience
Research Group:
Link to this item:
Official URL:
Export this item as:BibTeX
HTML Citation
Reference Manager


Repository Staff Only: item control page