Influence of Catalyst and Polymerization Conditions on the Properties of 1,3-Trimethylene Carbonate and ε-Caprolactone Copolymers

Pego, Ana Paula and Zhong, Zhiyuan and Dijkstra, Pieter J. and Grijpma, Dirk W. and Feijen, Jan (2003) Influence of Catalyst and Polymerization Conditions on the Properties of 1,3-Trimethylene Carbonate and ε-Caprolactone Copolymers. Macromolecular Chemistry and Physics, 204 (5-6). pp. 747-754. ISSN 1022-1352

PDF
Restricted to UT campus only: Request a copy
122Kb

Abstract:	The influence of the catalyst/initiator system and polymerization conditions on the microstructure and physical properties of copolymers of equimolar amounts of 1,3-trimethylene carbonate (TMC) and -caprolactone (CL) was studied. Statistical copolymers were prepared in the presence of stannous octoate (SnOct2) in the bulk at 80 °C (14 and 28 d) and 130 °C (1 and 3 d). The copolymerization of TMC and CL initiated by yttrium isopropoxide (Y5(µ-O)(OiPr)13) was performed in solution at room temperature (5 min) and in the bulk at 80 °C (2 min). Block copolymers, used as reference materials, were also prepared by sequential polymerization of the monomers in solution at room temperature with yttrium isopropoxide. Both SnOct2 and yttrium isopropoxide yielded polymers with shorter average monomer sequence lengths at higher reaction temperatures. For the polymerizations with SnOct2 a similar effect was observed when the reactions were allowed to proceed for longer periods of time. Independent of the catalyst/initiator system, the statistical copolymers prepared in the bulk at 80 or 130 °C were amorphous, with average monomer sequence lengths shorter than 3. The copolymer prepared in solution at room temperature with yttrium isopropoxide was more blocky, with CL sequences long enough to crystallize (Lcl=3.93). The former copolymers are highly flexible but show low tensile strengths, in agreement with their amorphous structure and low glass transition temperature. The latter copolymer is also flexible but much tougher and stiffer, as it is semi-crystalline. Its properties are characteristic of phase-separated block copolymers.
Item Type:	Article
Copyright:	© 2003 Wiley InterScience
Faculty:	Science and Technology (TNW)
Research Group:	Polymer Chemistry and BioMaterials (PBM) Biomaterials Science and Technology (BST)
Link to this item:	http://purl.utwente.nl/publications/71924
Official URL:	http://dx.doi.org/10.1002/macp.200390043
Export this item as:	BibTeX EndNote HTML Citation Reference Manager

Show download statistics for this publication

Repository Staff Only: item control page

Metis ID: 216723