Oxygen permeation through a Ce0.8Sm0.2O2−δ–La0.8Sr0.2CrO3−δ dual-phase composite membrane

Share/Save/Bookmark

Yi, Jianxin and Zuo, Yanbo and Liu, Wei and Winnubst, Louis and Chen, Chusheng (2006) Oxygen permeation through a Ce0.8Sm0.2O2−δ–La0.8Sr0.2CrO3−δ dual-phase composite membrane. Journal of Membrane Science, 280 (1-2). pp. 849-855. ISSN 0376-7388

[img]PDF
Restricted to UT campus only
: Request a copy
457Kb
Abstract:A composite of oxygen ion conducting oxide Ce0.8Sm0.2O2−δ (60 vol.%) and electron conducting oxide La0.8Sr0.2CrO3−δ was prepared by sintering a powder compact at a temperature of 1550 °C. No significant reaction between the two constituent oxides was observed under preparation and oxygen permeation conditions. Appreciable oxygen permeation fluxes through the composite membrane were measured at elevated temperatures with one side of it exposed to the ambient air and the other side to a flowing helium gas stream. The oxygen flux initially increased with time, and took a long time to reach a steady value. A steady oxygen permeation flux as high as 1.4 × 10−7 mol cm−2 s−1 was obtained with a 0.3 mm thick membrane at 950 °C under a relatively small oxygen partial pressure difference of 0.21 bar/0.0092 bar. It was revealed that the overall oxygen permeation process was mainly limited by the transport in the bulk of the membrane in the range of the membrane thickness greater than not, vert, similar1.0 mm, and the limitation by the surface oxygen exchange came into play at reduced thickness of not, vert, similar0.6 mm.
Item Type:Article
Copyright:Elsevier
Faculty:
Science and Technology (TNW)
Research Group:
Link to this item:http://purl.utwente.nl/publications/71893
Official URL:http://dx.doi.org/10.1016/j.memsci.2006.03.011
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 235224