Crystalline and disordered state of poly(dihexylsilylene) copolymers

Share/Save/Bookmark

Frey, Holger and Möller, Martin and Matyjaszewski, Krzysztof and Oelfin, Dieter (1995) Crystalline and disordered state of poly(dihexylsilylene) copolymers. Macromolecular Chemistry and Physics, 196 (4). pp. 1181-1194. ISSN 1022-1352

[img]
Preview
PDF
678Kb
Abstract:A systematic comparison of random copolymers, derived from poly(dihexylsilylene) (PDHS) by incorporation of monomeric units with shorter unbranched alkyl side chains, has been carried out based on calorimetry, variable temperature UV spectroscopy, and 29Si MAS (magic angle spinning) solid state NMR investigations. Also, hexylmethylsilylene units and branched monomers have been copolymerized. Up to 10% comonomer with shorter linear side chains (i. e., pentyl to propyl) could be incorporated into PDHS without impeding the all-trans order of the crystalline phase. In this case, the UV absorption maximum of the crystalline low-temperature phase was affected only slightly according to the length and fraction of the comonomer side chains. A less ordered crystal structure (λmax = 345-355 nm) was observed when the content of comonomers with shorter side chains was about 20%. Yet, all these materials form conformationally disordered mesophases. A clear disordering transition and corresponding thermochromism was not observed any more when 50% of propyl side chains were incorporated. The order of the crystalline and the mesophase is also strongly perturbed if only a small fraction (4%) of the side chains are branched at C2.
Item Type:Article
Copyright:© 1995 Wiley InterScience
Research Group:
Link to this item:http://purl.utwente.nl/publications/71207
Official URL:http://dx.doi.org/10.1002/macp.1995.021960417
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 106123