He, Y.J. and Winnubst, A.J.A. and Verweij, H. and Burggraaf, A.J. (1994) Sinter forging of zirconia toughened alumina. Journal of Materials Science, 29 (24). pp. 6505-6512. ISSN 0022-2461

open access
[img]
Preview
PDF
2MB
Abstract:Sinter forging experiments have been carried out on powder compacts of zirconia toughened alumina (ZTA) Ceramics Alumina-15 wt% zirconia was prepared by a gel precipitation method and calcined at temperatures of 900 or 1100°C. Full densification of ZTA ceramics was obtained within 15 min at 1400°C and 40 MPa. A homogeneous microstructure can be observed with an alumina grain size of 0.7 mgrm and a zirconia grain size of 0.2 mgrm. Almost no textural evolution occurred in the microstructure. During sinter forging the densification behaviour of the compacts was improved by an effective shear strain, for which values of more than 100% could be obtained. As a result of the shear deformation the densification of ZTA in the agr alumina phase stage shifted to lower temperature. During pressureless sintering the gamma to agr alumina transformation temperature was dependent of the preceding calcination temperature, while during sinter forging this phase transformation was independent of calcination temperature and took place at a lower temperature.
Item Type:Article
Copyright:© 1994 Springer Netherlands
Faculty:
Science and Technology (TNW)
Research Group:
Link to this item:http://purl.utwente.nl/publications/61574
Official URL:http://dx.doi.org/10.1007/BF00354012
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 106856