Tensile and elastic properties of segmented copolyetheresteramides with uniform aramid units

Share/Save/Bookmark

Niesten, M.C.E.J. and Gaymans, R.J. (2001) Tensile and elastic properties of segmented copolyetheresteramides with uniform aramid units. Polymer, 42 (14). pp. 6199-6207. ISSN 0032-3861

[img] PDF
Restricted to UT campus only
: Request a copy
317kB
Abstract:The tensile and elastic properties of segmented copolyetheresteramides with crystallisable aramid units of uniform length were investigated. The aramid concentration ranged from 3 to 30 wt%. The effect of type of poly(tetramethyleneoxide) (PTMO) segment, having a different tendency to crystallise, on the tensile and elastic properties was studied. The fracture stress of the polymers was found to be mainly affected by the degree of strain-induced crystallisation of the PTMO phase and the molecular weight of the polymers and not by the aramid content. The fracture strain of the polymers is exceptionally high, ranging from 1300 to 2200%. The shear modulus increased strongly with aramid content and ranged from 1.5 to 118 MPa. The uniform aramid units are very effective in forming physical crosslinks. The yield stress increased linearly with the aramid content. The yield stress and the log modulus are nearly linearly related for materials with these uniform length crystallisable units. The change of the modulus as a function of prestrain was studied. Up to 160–180% pre-strain the modulus decreases by a factor of 6–8, however, at higher strains the moduli increased again. The strong strain softening effect in the first 160% strain must be due the breaking up of the interconnecting lamellar structure. The healing of the modulus of strain-softened samples was studied with time. The healing was very slow. The materials, especially the low-modulus types, are highly elastic. The stress relaxation decreases with decreasing aramid content and the compression set was found to have a minimum at 9 wt% aramid. As expected, (strain-induced) PTMO crystallisation influences the elasticity and low-temperature flexibility negatively.
Item Type:Article
Copyright:© 2001 Elsevier Science
Research Group:
Link to this item:http://purl.utwente.nl/publications/61373
Official URL:http://dx.doi.org/10.1016/S0032-3861(01)00088-X
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 205525