Ferrocenyl-Functionalized Silica Nanoparticles: Preparation, Characterization, and Molecular Recognition at Interfaces

Share/Save/Bookmark

Ling, Xing Yi and Reinhoudt, David N. and Huskens, Jurriaan (2006) Ferrocenyl-Functionalized Silica Nanoparticles: Preparation, Characterization, and Molecular Recognition at Interfaces. Langmuir, 22 (21). pp. 8777-8783. ISSN 0743-7463

[img]PDF
Restricted to UT campus only
: Request a copy
424Kb
Abstract:Ferrocenyl-functionalized silica nanoparticles (Fc-SiO2, 6a-6c) of about 60 nm with supramolecular "guest" properties were prepared. Nanoparticles 6a-6c differed by the addition of different molar ratios of starting compounds during the functionalization step, i.e., 1:0, 1:10, and 1:90 of 2-ferrocenyl amidoethoxyethanol and diethylene glycol for 6a, 6b, and 6c, respectively. X-ray photoelectron spectroscopy (XPS) proved the presence of ferrocenyl groups on the surfaces of 6a-6c, whereas the elemental analysis revealed an iron content of particles 6a-6c of 0.10-0.16%. Dynamic light scattering (DLS) results showed that, compared with 6a, 6b dispersed well in aqueous media, possibly due to the presence of diethylene glycol at the surfaces of 6b that significantly increases its overall hydrophilicity. Cyclic voltammetry of 6b indicated a totally irreversible system and a "mixed" diffusion-adsorption behavior, which is attributed to sluggish electron transfer. The shifted Ip,C/Ip,A* ratio showed that the ferrocenyl groups are robustly attached to the nanoparticle surface within the experimental potential range. The supramolecular recognition of Fc-SiO2 nanoparticles at interfaces was verified by their adsorption on B-cyclodextrin (B-CD) self-assembled monolayers, as monitored by surface plasmon resonance (SPR) spectroscopy. The ability of the Fc-SiO2 nanoparticles to form host-guest interactions was also demonstrated by the attachment of B-CD-functionalized Au nanoparticles (2.8 nm) on the Fc-SiO2 surfaces, when mixed in solution.
Item Type:Article
Copyright:© 2006 American Chemical Society
Faculty:
Science and Technology (TNW)
Research Group:
Link to this item:http://purl.utwente.nl/publications/59347
Official URL:http://dx.doi.org/10.1021/la0610497
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 236564