Selective Etching of Semicrystalline Polymers: CF4 Gas Plasma Treatment of Poly(ethylene)

Share/Save/Bookmark

Olde Riekerink, M.B. and Terlingen, J.G.A. and Engbers, G.H.M. and Feijen, J. (1999) Selective Etching of Semicrystalline Polymers: CF4 Gas Plasma Treatment of Poly(ethylene). Langmuir, 15 (14). pp. 4847-4856. ISSN 0743-7463

[img] PDF
Restricted to UT campus only
: Request a copy
302kB
Abstract:A series of poly(ethylene) (PE) films with different degrees of crystallinity was treated with a radio-frequency tetrafluoromethane (CF4) gas plasma (48-49 W, 0.06-0.07 mbar, and continuous vs pulsed treatment). The etching behavior and surface chemical and structural changes of the PE films were studied by weight measurements, X-ray photoelectron spectroscopy (XPS), static and dynamic water contact angle measurements, scanning electron microscopy (SEM), and atomic force microscopy (AFM). With increasing crystallinity (14-59%) of PE, a significant and almost linear decrease of the etching rate was found, ranging from 50 Å/min for linear low-density poly(ethylene) (LLDPE) to 35 Å/min for high-density poly(ethylene) (HDPE). XPS analysis revealed that after CF4 plasma treatment the PE surfaces were highly fluorinated up to F/C ratios of 1.6. Moreover, CF4 plasma treatment of PE resulted in extremely hydrophobic surfaces. Advancing water contact angles up to 150 were measured for treated LDPE films. Both SEM and AFM analysis revealed that pronounced surface restructuring took place during prolonged continuous plasma treatment (15 min). The lamellar surface structure of LDPE changed into a nanoporous-like structure with uniform pores and grains on the order of tens of nanometers. This phenomenon was not observed during plasma treatment of HDPE films. Apart from surface roughening due to selective etching, pulsed plasma treatment did not result in significant surface structural changes either. Therefore, the restructuring of continuously plasma-treated surfaces was attributed to a combined effect of etching and an increase of the surface temperature, resulting in phase separation of PE-like and poly(tetrafluoroethylene)-like material, of which the latter is surface oriented.
Item Type:Article
Copyright:© 1999 American Chemical Society
Faculty:
Science and Technology (TNW)
Research Group:
Link to this item:http://purl.utwente.nl/publications/59288
Official URL:http://dx.doi.org/10.1021/la990020i
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 105680