Microporous Niobia-Silica Membrane with Very Low CO2 Permeability

Share/Save/Bookmark

Boffa, Vittorio and Elshof, Johan E. ten and Petukhov, Andrei V. and Blank, Dave H.A. (2008) Microporous Niobia-Silica Membrane with Very Low CO2 Permeability. ChemSusChem, 1 (5). pp. 437-443. ISSN 1864-5631

[img] PDF
Restricted to UT campus only
: Request a copy
320kB
Abstract:A sol-gel-derived microporous ceramic membrane with an exceptionally low permeability for CO2 from gaseous streams was developed and characterized. The sols were prepared from a mixture of niobium and silicon alkoxide precursors by acid-catalyzed synthesis. Microporous films were formed by coating asymmetric -alumina disks with the polymeric sol (Si/Nb=3:1), followed by calcination at 500 °C. The membrane consists of a 150-nm-thick layer with a Si/Nb atomic ratio of about 1.5. The single-gas permeance of small gas molecules such as H2, CH4, N2, and SF6 decreases steadily with kinetic diameter. Hydrogen, helium, and carbon dioxide follow an activated transport mechanism through the membrane. The permeance of CO2 in this membrane is much lower than that in pure silica, and its behavior deviates strongly from the general trend observed with the other gases. This is attributed to a relatively strong interaction between CO2 and adsorption sites in the niobia-silica membrane.
Item Type:Article
Copyright:© 2008 Wiley InterScience
Faculty:
Science and Technology (TNW)
Research Group:
Link to this item:http://purl.utwente.nl/publications/59173
Official URL:http://dx.doi.org/10.1002/cssc.200700165
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 250713