Moulded photoplastic probes for near-field optical applications

Share/Save/Bookmark

Kim, B.J. and Flamma, J.W. and Have, E. ten and Garcia-Parajo, M.F. and Hulst, N.F. van and Brugger, J. (2001) Moulded photoplastic probes for near-field optical applications. Journal of Microscopy, 202 . pp. 16-21. ISSN 0022-2720

[img] PDF
Restricted to UT campus only
: Request a copy
268kB
Abstract:The inexpensive fabrication of high-quality probes for near- field optical applications is still unsolved although several methods for integrated fabrication have been proposed in the past. A further drawback is the intensity loss of the transmitted light in the 'cut-off' region near the aperture in tapered optical fibres typically used as near-field probes. As a remedy for these limitations we suggest here a new wafer- scale semibatch microfabrication process for transparent photoplastic probes. The process starts with the fabrication of a pyramidal mould in silicon by using the anisotropic etchant potassium hydroxide. This results in an inverted pyramid limited by <111 > silicon crystal planes having an angle of similar to 54 degrees. The surface including the mould is covered by a similar to 1.5 nm thick organic monolayer of dodecyltrichlorosilane (DTS) and a 100-nm thick evaporated aluminium film. Two layers of photoplastic material are then spin-coated (thereby conformal filling the mould) and structured by lithography to form a cup for the optical fibre microassembly. The photoplastic probes are finally lifted off mechanically from the mould with the aluminium coating. Focused ion beam milling has been used to subsequently form apertures with diameters in the order of 80 nm. The advantage of our method is that the light to the aperture area can be directly coupled into the probe by using existing fibre-based NSOM set- ups, without the need for far-field alignment, which is typically necessary for cantilevered probes. We have evidence that the aluminium layer is considerably smoother compared to the 'grainy' layers typically evaporated o­n free-standing probes. The optical throughput efficiency was measured to be about 10(-4). This new NSOM probe was directly bonded to a tuning fork sensor for the shear force control and the topography of a polymer sample was successfully obtained.
Item Type:Article
Copyright:© 2001 Blackwell
Research Group:
Link to this item:http://purl.utwente.nl/publications/36491
Official URL:http://dx.doi.org/10.1046/j.1365-2818.2001.00820.x
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 202095