Preparation of YBaCuO thin films on various substrates by laser ablation: influence of the substrate temperature

Share/Save/Bookmark

Blank, D.H.A. and Adelerhof, D.J. and Flokstra, J. and Rogalla, H. (1990) Preparation of YBaCuO thin films on various substrates by laser ablation: influence of the substrate temperature. Physica C: Superconductivity, 167 (3-4). pp. 423-432. ISSN 0921-4534

[img]
Preview
PDF
839Kb
Abstract:High-quality YBa2Cu3O7¿¿ films were prepared in situ by laser ablation on SrTiO3 (100), on MgO (100) and on Si (111) + ZrO2 buffer layer. We especially investigated the influence of the substrate temperature. In similar preparation circumstances zero resistivity has been achieved for films on SrTiO3 up to 89.5 K, on MgO up to 84.6 K and on Si(+ZrO2) up to 83.5 K. X-ray diffraction analysis was used to study the growth conditions of the films, and to determine the oxygen stoichiometry. The films deposited at substrate temperatures above 720°C show pure c-axis orientation with an oxygen deficiency ¿<0.1. Interdiffusion between substrate and layer, analyzed with Auger sputter profiling, could not be observed. The grains of the films on Si+ZrO2, studied by scanning electron microscopy, are caused by the polycrystalline buffer layer. These grains largely determine the physical properties of the deposited layer.

Critical current measurements were carried out using wet chemically etched microbridges on the different substrates. At T=77 K the values are in the range from 3x106 A/cm2 for films on SrTiO3 to 2x103 A/cm2 in the case of Si+ZrO2. The extrapolated resistivity at T=0 is found to be proportional to the temperature width of the superconducting transition.
Item Type:Article
Copyright:© 1990 Elsevier Science B.V
Faculty:
Science and Technology (TNW)
Research Group:
Link to this item:http://purl.utwente.nl/publications/24329
Official URL:http://dx.doi.org/10.1016/0921-4534(90)90363-J
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 129129