Ordering of vacancies on Si(001)

Share/Save/Bookmark

Zandvliet, H.J.W. (1997) Ordering of vacancies on Si(001). Surface Science, 377-37 . pp. 1-6. ISSN 0039-6028

open access
[img]
Preview
PDF
873kB
Abstract:Missing dimer vacancies are always present on the clean Si(001) surface. The vacancy density can be increased by ion bombardment (Xe+, Ar+), etching (O2, Br2, I2, etc.) or Ni contamination. The equilibrium shape at low vacancy concentrations (<0.2¿0.3 monolayers) of these vacancy islands is elongated in a direction perpendicular to the dimer rows of the upper terrace, whereas for higher vacancy concentrations the equilibrium shape is rotated by 90°. The absence of dimerisation within the narrow vacancy islands at low vacancy concentration alone is not sufficient to explain this shape transformation, therefore it is suggested that the specific rebonding of these structures also plays a role. A more detailed analysis of the annealing behaviour, width, spacing between and depth of the elongated low-vacancy concentration vacancy islands reveals that the Ni-induced vacancy islands differ significantly from the etching-induced vacancy islands.
Item Type:Article
Copyright:© 1997 Elsevier Science
Faculty:
Science and Technology (TNW)
Research Group:
Link to this item:http://purl.utwente.nl/publications/23850
Official URL:http://dx.doi.org/10.1016/S0039-6028(96)01316-7
Export this item as:BibTeX
EndNote
HTML Citation
Reference Manager

 

Repository Staff Only: item control page

Metis ID: 128649