Electrode polarization at the Au, O2(g)/Fe implanted yttria-stabilized zirconia interface


Hassel, B.A. van and Boukamp, B.A. and Burggraaf, A.J. (1992) Electrode polarization at the Au, O2(g)/Fe implanted yttria-stabilized zirconia interface. Solid State Ionics, 51 (3-4). pp. 161-174. ISSN 0167-2738

open access
Abstract:Ion implantation has been applied to modify the surface properties of yttria-stabilized zirconia (YSZ). A three-electrode cell was used for measuring steady state current-overpotential curves and for determining the electrode impedance. An increase of the equilibrium exchange current density at the Au, O2(g)/yttria stabilized zirconia interface with a factor 10–50 has been observed after the implantation of 15 kV 56Fe up to a dose of 8 × 1016 at.cm−2. This increase results from a broadening of the active surface area due to an increase in the electronic conductivity of the Fe implanted YSZ surface and from an increase of the fraction of coverage of the adsorbed oxygen molecules. The double layer capacitance of the Au, O2,g/YSZ interface increases with a factor 10–100 after the Fe implantation. This is most likely due to the variable oxidation state of the implanted Fe ions, thus providing an additional way for charge accumulation. In comparison with the not implanted Au, O2,g/YSZ interface no changes in the rate-determining steps of the oxygen exchange mechanism occur after Fe implantation. Similar apparent charge-transfer coefficients have been determined. A slight decrease in the oxygen partial pressure dependence of Io is observed. The experimental results can still be explained with a reaction model where the charge-transfer process is in competition with the surface diffusion of molecular adsorbed oxygen species along the noble metal-solid electrolyte interface. At cathodic and anodic overpotentials inductive effects appear at low frequencies in the impedance diagram. The inductive effects result from a charge-transfer mechanism where a step-wise transfer of electrons to adsorbed oxygen species takes place.
Item Type:Article
Copyright:© 1992 Elsevier Science
Research Group:
Link to this item:http://purl.utwente.nl/publications/12632
Official URL:https://doi.org/10.1016/0167-2738(92)90195-U
Export this item as:BibTeX
HTML Citation
Reference Manager


Repository Staff Only: item control page

Metis ID: 106813